| PARALOID®
Acrylic Resins Thermoplastics |
| |
|
RESIN
PROPERTIES |
PRODUCT
AS SUPPLIED |
PRODUCT
NAME |
APPLICATION NOTES |
Tg
(°C) |
BASE
COMPOSITION |
SOLUBILITY
PARAMETER |
MOLECULAR
WEIGHT
(Mw) |
SOLIDS
(%) |
SOLVENT
RATIO |
DENSITY
(lb/gal) |
VISCOSITY
(cP) |
| GENERAL
THERMOPLASTICS |
| A-11, 100% |
Hard resin;
resistant to water & alcohol |
100
|
MMA |
9.4 |
125,000 |
powder |
- |
9.8 |
|
| A-12,
100% |
|
90
|
|
|
90,000 |
pellets |
- |
9.8 |
|
| A-101,
40% |
Hard resin;
exterior durability & resistance |
105 |
MMA |
9.4 |
100,000 |
40 |
MEK |
7.8 |
5,000 |
| A-10S,
30% |
properties; |
|
|
|
70,000 |
30 |
PMAc |
8.6 |
1,000 |
| A-646 |
A-646 has
enhanced gloss, reflow |
|
|
|
40,000 |
45 |
MEK |
8.1 |
2,200 |
| B-60,
100% |
Fast dry;
adhesion to plastics |
75 |
MMA/BMA |
9.2 |
50,000 |
powder |
- |
9.4 |
|
| B-64,
100% |
General purpose,
concrete & exterior durability |
60 |
MMA/EA |
9.8 |
140,000 |
pellets |
- |
9.3 |
|
| B-66,
100% |
General purpose;
fast solvent release |
50 |
MMA/BMA |
9.0 |
70,000 |
powder |
- |
9.2 |
|
| B-66T,
51% |
|
|
|
|
|
51 |
Tol |
8.2 |
3,300 |
| B-66X,
51% |
|
|
|
|
|
51 |
Xyl |
8.2 |
6,800 |
| B-72,
100% |
Compatible with
various resin types; soft resin |
40 |
EMA
cop. |
9.3 |
105,000 |
pellets |
- |
9.6 |
|
| B-72,
50% |
|
|
|
|
|
50 |
Tol |
8.3 |
4,000 |
| B-82,
100% |
General purpose;
chemical resistant; softest resin |
35 |
MMA/EA |
9.4 |
120,000 |
pellets |
- |
9.7 |
|
| B-82,
51% |
|
|
|
|
|
51 |
Tol |
8.3 |
5,500 |
| THERMOPLASTICS
WITH ENHANCED ADHESION |
| A-21,
100% |
Hardest resin;
Improved intercoat adhesion |
105 |
MMA |
9.4 |
120,000 |
powder |
- |
9.8 |
|
| A-21,
30% |
|
|
|
|
|
30 |
Tol/BuOH,
90/10 |
7.8 |
400 |
| A-21LV |
|
|
|
|
|
30 |
Tol/MEK/BuOH
50/40/10 |
7.8 |
350 |
| B-44,
100% |
Excellent
adhesion to various untreated |
60 |
MMA/EA |
9.8 |
140,000 |
pellets |
- |
9.8 |
|
| B-44S,
40% |
substrates; PVDF
coatings |
|
|
|
|
40 |
Tol |
8.1 |
1,500 |
| B-48N,
100% |
Unique hardness
vs. flexibility; adhesion |
50 |
MMA/BA |
9.3 |
250,000 |
pellets |
- |
9.6 |
|
| B-48S,
45% |
to untreated
metals |
|
|
|
|
45 |
Tol |
8.1 |
8,500 |
| B-84,
45% |
Unique airdry
adhesion to problem surfaces |
50 |
MMA/BA |
9.3 |
80,000 |
45 |
Tol/sBuOH,
85/15 |
8.1 |
5,000 |
| ALKYD
MODIFIERS, DISPERSANTS |
| B-67,
100% |
Medium & long
oil alkyd modifier; most |
50 |
IBMA |
8.6 |
60,000 |
pellets |
- |
8.7 |
|
| B-67,
45% |
water resistant;
general purpose thermoplastic |
|
|
|
60,000 |
45 |
VMP-N/Xyl,
90/10 |
7.3 |
1,500 |
| B-67MT |
|
|
|
|
30,000 |
45 |
MT |
7.3 |
1,200 |
| B-99N,
100% |
Improve gloss of
other resins; short & |
80 |
MMA/BMA |
9.4 |
15,000 |
pellets |
- |
9.6 |
|
| B-99,
50% |
medium oil alkyd
compatible; pigment dispersant |
|
|
|
|
50 |
Xyl/Tol,
70/30 |
8.4 |
3,000 |
| XR-34 |
Broad alkyd
compatibility; pigment dispersant |
80 |
MMA/BMA |
9.1 |
30,000 |
50 |
Xyl |
8.5 |
3,000 |
| B-1225 |
Modifier for
high-solids alkyds; pigment dispersant |
60 |
MMA/BMA |
8.8 |
5,000 |
65 |
Xyl |
8.3 |
6,000 |
| DM-55,
100% |
Excellent pigment
dispersant |
70 |
MMA
cop. |
9.4 |
6,000 |
pellets |
- |
8.9 |
|
| NAD-10V |
Non-aqueous
dispersion; fluorescent pigments |
40 |
IBMA |
|
130,000 |
40 |
VMP-N |
7.1 |
500 |
| F-10 |
Aliphatic
hydrocarbon soluble; fluorescent pigments |
20 |
BMA |
8.8 |
150,000 |
40 |
MT/A150,
87/13 |
7.4 |
2,100 |
Solvents:
Tol = tolune PMAc = PM Acetate MEK
= methyl ethyl ketone VMP-N = VM&P Naptha MT
= Mineral thinner
Xyl = xylene BuOH = butanol s-BuOH
= sec-butanol A150 = Aromatic 150 cop.
= copolymer
| PARALOID®
Acrylic Resins Thermosets
& Polyols |
| |
|
RESIN
PROPERTIES |
PRODUCT
AS SUPPLIED |
PRODUCT NAME |
APPLICATION NOTES |
Tg
(°C) |
MOLECULAR
WEIGHT
(Mw) |
ACID
NUMBER
(solids) |
HYDROXYL
EQUIVALENT
WEIGHT
(solids) |
SOLIDS
(%) |
SOLVENT RATIO |
DENSITY
(lb/gal) |
VISCOSITY
(cP) |
| POLYOLS
FOR ACRYLIC URETHANE RESINS, CONVENTIONAL VOC COATINGS |
| AU-1033 |
Low isocyanate
demand with lacquer-like drying properties |
65 |
35,000 |
<2 |
1000 |
50 |
PMAc/EB/VMP-N,
55/25/20 |
8.5 |
6,000 |
| AU-1164 |
100% solids;
hard resistant durable coatings |
50 |
20,000 |
<2 |
700 |
pellets |
– |
9.7 |
|
| AU-2608 |
Excellent
cost/performance balance |
60 |
18,000 |
3 |
680 |
60 |
Xyl |
8.5 |
7,200 |
| AU-608S |
High
performance general product finishing |
55 |
20,000 |
10 |
650 |
60 |
PMAc/Tol,
65/35 |
8.8 |
6,500 |
| AU-608B |
supplied in
several different solvents |
|
|
|
|
60 |
nBuAc |
8.6 |
4,500 |
| AU-608X |
|
|
|
|
|
58 |
Xyl |
8.5 |
6,200 |
| POLYOLS
FOR HIGH SOLIDS, LOW VOC COATINGS |
| AU-1453 |
Formulates well
to low VOC. Best overall balance of properties. |
45 |
10,000 |
<2 |
460 |
70 |
nBuAc |
8.9 |
4,500 |
| AU-946 |
High crosslink
density potential for high performance coatings |
50 |
7,500 |
<2 |
420 |
67 |
MAK |
8.6 |
8,500 |
| AU-1166 |
Low isocyanate
demand |
40 |
9,000 |
<2 |
1000 |
73 |
nBuAc |
8.8 |
8,000 |
| AU-1468 |
Low isocyanate
demand with excellent adhesion |
10 |
12,000 |
8 |
900 |
80 |
nBuAc/EEP,80/20 |
8.7 |
7,000 |
| HYDROXYL
FUNCTIONAL FOR MELAMINE RESINS, CONVENTIONAL VOC COATINGS |
| AT-746 |
Hardest finish
of AT line |
75 |
45,000 |
15 |
1305 |
50 |
Xyl |
8.2 |
6,000 |
| AT-63 |
Fast curing;
high gloss and durability |
25 |
|
30 |
1305 |
50 |
Xyl |
8.0 |
2,300 |
| HYDROXYL
RESINS FOR HIGH SOLIDS, LOW VOC COATINGS |
| AT-410 |
High-solids
AT-63 analog |
30 |
9,000 |
25 |
710 |
73 |
MAK |
8.4 |
4,000 |
| AT-400 |
Outstanding
chemical resistance |
15 |
15,000 |
25 |
560 |
75 |
MAK |
8.5 |
6,000 |
| CARBOXYL
FUNCTIONAL FOR EPOXY RESINS FOR OVEN BAKE, CONVENTIONAL VOC COATINGS |
| AT-81 |
Excellent
adhesion and gloss for metal deco; |
40 |
45,000 |
65 |
|
56 |
A150/EGBE,
87/13 |
8.4 |
11,700 |
| AT-147 |
often
mixed 1:1 with AT-85 (AT-148) |
|
|
|
|
55 |
EGBE |
8.5 |
6,000 |
| AT-9LO |
General resin
for can coatings and metal deco |
30 |
50,000 |
35 |
|
43 |
A150/EGBE,
83/17 |
8.1 |
5,000 |
| AT-76 |
Balance of
fabrication & processing resistance |
25 |
65,000 |
38 |
|
41 |
A150/EGBE,
75/25 |
8.1 |
3,500 |
| AT-85 |
Softest and
most flexible carboxyl resin |
10 |
35,000 |
65 |
|
56 |
A150/EGBE,
87/13 |
8.6 |
5,300 |
| AT-148 |
|
|
|
|
|
55 |
EGBE |
8.3 |
2,400 |
| CARBOXYL
RESIN FOR AMBIENT CURE, LOW VOC COATINGS |
| AE-1285 |
Ambient
crosslink with epoxies; close to urethane performance |
20 |
6,500 |
49 |
|
69 |
Xyl/BuOH
70/30 |
9.0 |
4,500 |
| MISCELLANEOUS |
WR-97
Water
Reducible |
High gloss;
solvent and water compatible; melamine crosslinking |
12 |
30,000 |
39 |
1300 |
70 |
IPOH/EGBE,
83/17 |
8.4 |
13,700 |
Reactive
Mod
QM-1007M* |
Used to raise
solids and reduce VOC; compatible with acrylic & polyester polyols |
|
|
|
100 |
98 |
Hep |
8.8 |
50 |
* Not available in European Region
Solvents:
Tol = tolune PMAc = PM Acetate MAK
= methyl amyl ketone EB = ethyl benzene EGBE
= Ethyleneglycol butylether
Xyl = xylene nBuOH = butanol IPOH
= isopropyl alcohol A150 = Aromatic 150
VMP-N = VM&P Naphtha
Hep = heptane nBuAc = n-butyl acetate EEP
= ethyl-3-ethoxypropionate
|